Brand

Alkali Resistant Castable

WAC

Refractoriness ( ℃ )

≥ 1690

Bulk Density (g/cm 3 )

≥ 2.0

Chemical Composition Al 2 O 3 (%)

≥ 40

Bending Strength

(MPa)

110 ℃

After drying at

≥ 50

℃ × 3h

After firing at

1300

≥ 35

℃ × 3h

Linear change rate after firing (%)

1300

± 0.5

Service Temperature ( ℃ )

1300

Characteristics

Good alkali resistance , high strength long service time.

Application

Used in cement rotary kiln